Products > Copper Alloys > C95400 Products > C95400 Properties
MO1 - As Sand Cast
Tensile Strength:
Yield  Strength:
Elongation:
Brinell Hardness:

M02 - As Centrifugal Cast
Tensile Strength:
Yield Strength:
Elongation:
Brinell Hardness:

M07 - As Continuous Cast
Tensile Strength:
Yield Strength:
Elongation:
Minimum 85 ksi     
Minimum 35 ksi - 0.5% Ext. under load         
Minimum 18% in 2 in.           
170   3000 kg load


Minimum 75 ksi
Minimum 30 ksi - 0.5% Ext. under load
Minimum 12% in 2 in.           
150   3000 kg load


Minimum 85 ksi
Minimum 32 ksi - 0.5% Ext. under load
12%, in 2 inches
Chemical Composition  (%max., unless shown as range or min.)   
Need to send a drawing?
We are now accepting the following file types:
    Cu                 Al              Fe      Mn   Ni(1)
Min./Max.  83.0 min    10.0-11.5   3.0-5.0   .50   1.5 
Nominal    83.2            10.8             4.0           -        - 


(1) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
Joining Techniques
Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welded
Coated Metal Arc Welding
Machinability Rating
Suitability
Good
Good
Not Recommended  
Good
Good 
60
Mechanical Properties (measured at room temperature, 68 F (20 C) 
Fabrication Properties  (Common fabrication process - Casting)
Physical Properties  

Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Magnetic Permeability* 
Magnetic Permeability** 
US Customary
1900 F 
1880 F 
0.269 lb/in3 at 68 F
7.45
80.2 ohms-cmil/ft @ 68 F
13 %IACS @ 68 F
33.9 Btu · ft/(hr · ft2·oF)at 68F 
9.0 ·10-6 per oF (68-572 F) 
0.1 Btu/lb/oF at 68 F 
155000 ksi 
1.2
1.27

Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Magnetic Permeability* 
Magnetic Permeability** 
Metric
1038 C 
1027 C 
7.45 gm/cm3 @ 20 C
7.45
13.33 microhm-cm @ 20 C
0.075 MegaSiemens/cm @ 20 C
58.7 W/m · oK at 20 C 
16.2 ·10-6 per oC (20-300 C) 
419.0 J/kg · oK at 293 K 
107000 MPa
1.2
1.27
*TQ 50 Temper, Field Sterngth 16 kA/m 
**As Cast, Field Strength 16 kA/m