H02 - Rod / Bar -
Tensile Strength:
Yield Strength:
Elongation:
Rockwell Hardness B Scales:
118 ksi
75 ksi - 0.5% Ext. under load
15%
98
Chemical Composition (%max., unless shown as range or min.)
Need to send a drawing?
We are now accepting the following file types:
Cu(1) Al Fe Mn Ni(2) Si Sn Zn Min./Max. Rem. 9.0-11.0 2.0-4.0 1.5 4.0-5.5 .25 .20 .30
Nominal 80 10.0 3.5 1.0 - - - -
(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
Joining Techniques
Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welded
Coated Metal Arc Welding
Spot Weld
Seam Weld
Butt Weld
Capacity for Being Cold Worked
Capacity for Being Hot Formed
Forgeability Rating
Machinability Rating
Suitability
Not Recommended
Fair
Not Recommended
Good
Good
Good
Good
Good
Poor
Good
75
30
Mechanical Properties (measured at room temperature, 68 F (20 C)
Fabrication Properties
Typical for 1" Rod Half Hard (20%) Temper
Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
US Customary
1930 F
1895 F
0.274 lb/in3 at 68 F
7.58
116.0 ohms-cmil/ft @ 68 F
7 %IACS @ 68 F
22.6 Btu · ft/(hr · ft2·oF)at 68F
9.0 ·10-6 per oF (68-572 F)
0.09 Btu/lb/oF at 68 F
17500 ksi
6400 ksi
Physical Properties
Melting Point - Liquidus
Melting Point - Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Modulus of Rigidity
Metric
1054 C
1035 C
7.58 gm/cm3 @ 20 C
7.58
19.28 microhm-cm @ 20 C
0.041 MegaSiemens/cm @ 20 C
39.1 W/m · oK at 20 C
16.2 ·10-6 per oC (20-300 C)
377.1 J/kg · oK at 293 K
121000 MPa
44130 MPa
| ||||
Click to get a quote: